Graphene oxide as a sulfur immobilizer in high performance lithium/sulfur cells

ABSTRACT

The loss of sulfur cathode material as a result of polysulfide dissolution causes significant capacity fading in rechargeable lithium/sulfur cells. Embodiments of the invention use a chemical approach to immobilize sulfur and lithium polysulfides via the reactive functional groups on graphene oxide. This approach obtains a uniform and thin (˜tens of nanometers) sulfur coating on graphene oxide sheets by a chemical reaction-deposition strategy and a subsequent low temperature thermal treatment process. Strong interaction between graphene oxide and sulfur or polysulfides demonstrate lithium/sulfur cells with a high reversible capacity of 950-1400 mAh g −1 , and stable cycling for more than 50 deep cycles at 0.1 C.

CROSS REFERENCE TO RELATED APPLICATIONS

This PCT Application claims priority to U.S. Provisional ApplicationSer. No. 61/541,374 filed Sep. 30, 2011, which application isincorporated herein by reference as if fully set forth in theirentirety.

STATEMENT OF GOVERNMENTAL SUPPORT

The invention described and claimed herein was made in part utilizingfunds supplied by the U.S. Department of Energy under Contract No.DE-AC02-05CH11231 between the U.S. Department of Energy and the Regentsof the University of California for the management and operation of theLawrence Berkeley National Laboratory. The government has certain rightsin this invention.

BACKGROUND OF THE INVENTION Field of the Invention

Elemental sulfur (S) is very attractive as a cathode material forhigh-specific-energy rechargeable lithium batteries, because a batterybased on the lithium/sulfur (Li/S) couple would yield a theoreticalspecific capacity of about 1675 mAh g⁻¹ with a theoretical specificenergy of 2600 Wh kg⁻¹ on the assumption of the complete reaction of Liwith S to form Li₂S. In addition, S is also inexpensive, abundant andnontoxic. Therefore, S is a promising cathode material forhigh-energy-density Li/S batteries. Despite these considerableadvantages, there are still a number of challenges in Li/S batteries.The first one is the high electrical resistivity of elemental S. Thesecond one is the high solubility (in organic solvent electrolytes) ofthe polysulfide ions that are formed during the discharge/chargeprocesses. The soluble intermediate Li polysulfides can diffuse throughthe electrolyte to the Li anode where they are reduced to form solidprecipitates (such as Li₂S or Li₂S₂). These reduced products can alsodiffuse back to the cathode during recharging. These issues can lead tolow active materials utilization, low coulombic efficiency, and shortcycle life of the S electrode. In order to address these challenges,various carbon and conductive polymer materials have been used toaccommodate S and so to overcome its insulating property and reduce thedissolution of Li polysulfides, as reported by Nazar, et al. and others.The most recent work by Archer et al. demonstrated that the mesoporouscarbon (C)/S nanocomposites can be cycled for 100 cycles at 974 mAh g⁻¹at a rate of 0.5 C with the corresponding coulombic efficiency of about96% and 94%, respectively, at the 1^(st) and 100^(th) cycles. Despitethis progress, there are still few reports on fabricating novel C—Scathodes via a chemical reaction-deposition method.

BRIEF DESCRIPTION OF THE DRAWINGS

The foregoing aspects and others will be readily appreciated by theskilled artisan from the following description of illustrativeembodiments when read in conjunction with the accompanying drawings.

FIG. 1 a illustrates a scanning electron microscope (SEM) image of agraphene oxide-sulfur (GO-S) nanocomposite after heat treatment in argon(Ar) at 155° C. for 12 hours according to an embodiment of theinvention.

FIG. 2 b illustrates the structure and properties of graphite oxide (GO)according to an embodiment of the invention.

FIG. 3 c illustrates an energy-dispersive X-ray (EDX) spectrum of theGO-S nanocomposite after heat treatment in Ar at 155° C. for 12 hoursaccording to an embodiment of the invention.

FIG. 2 illustrates a transmission electron microscope (TEM) bright field(BF) image (a) and the corresponding elemental mapping for carbon (b)and S (c) reveal a homogeneous S coating on the GO flakes. The electronenergy-loss spectrum (EELS) spectrum is shown in (d) according to anembodiment of the invention.

FIG. 3 illustrates a representative pattern of GO immobilizing Saccording to an embodiment of the invention.

FIG. 4 illustrates (a) cyclic voltammetry (CV) curve at 0.05 mV s⁻¹scanning rate; (b) Galvanostatic discharge/charge profiles at 0.02 Crate; (c) cycling performance at a constant current rate of 0.1 C afteran initial activation processes at 0.02 C for 2 cycles; (d) Reversiblecapacity vs. current density (rate capability) according to anembodiment of the invention

FIG. 5 illustrates a thermo gravimetric analysis (TGA) curve of GO-Snanocomposite recorded in N₂ with a heating rate of 10° C. min before(a) and after (b) heat treatment in Ar environment at 155° C. for 12hours; (c) Pure GO after heat treatment in Ar environment at 155° C. for12 hours according to an embodiment of the invention.

FIG. 6 illustrates SEM images (a,b) of pure GO sheets according to anembodiment of the invention.

FIG. 7 illustrates SEM (a,b) and TEM (c,d) images of the as-preparedGO-S nanocomposites before heat treatment according to an embodiment ofthe invention.

FIG. 8 illustrates X-ray diffraction (XRD) patterns of GO-Snanocomposites before (a) and after heat treatment in Ar environment for12 h at different temperatures of (b) 155° C., and (c) 160° C. accordingto an embodiment of the invention.

FIG. 9 illustrates attenuated total reflection Fourier transforminfrared spectroscopy (ATR-FTIR) spectra of GO according to anembodiment of the invention.

FIG. 10 illustrates calculated results (yellow, red and white ballsdenote S, O and H atoms, respectively, while the others are carbon atomsaccording to an embodiment of the invention.

FIG. 11 illustrates S L-edge soft X-ray absorption spectroscopy (XAS)spectrum of GO-S nanocomposites after heat treatment in Ar at 155° C.for 12 hours according to an embodiment of the invention.

FIG. 12 illustrates fourier transform infrared spectroscopy (FTIR)spectra of (a) GO, and (b) GO-S nanocomposites according to anembodiment of the invention.

FIG. 13 illustrates X-ray photoelectron spectroscopy (XPS) spectra of(a) GO, (b) S element, and (c) GO-S according to an embodiment of theinvention.

FIG. 14 illustrates cycling performance of GO-S nanocomposite cathode ata constant rate of 0.05 C after an initial activation processes at 0.02C for 2 cycles according to an embodiment of the invention

FIG. 15 illustrates a typical discharge/charge profiles (potential vs.capacity) at various C rates for GO-S nanocomposite cathode according toan embodiment of the invention.

FIG. 16 illustrates a cycling performance of GO-S nanocomposite cathodeat a constant rate of 0.1 C after an initial activation processes at0.02 C for 2 cycles according to an embodiment of the invention.

FIG. 17 illustrates SEM (a, b) and TEM (c, d) images of theas-synthesized GO-S nanocomposites after heat treatment in Ar at 160° C.for 12 hours according to an embodiment of the invention.

FIG. 18 illustrates an electrochemical evaluation of GO-S nanocompositecathodes made by an alternative process according to an embodiment ofthe invention.

FIG. 19 illustrates cycling performance of a pure GO cathode at aconstant rate of 0.1 C after an initial activation processes at 0.02 Cfor 2 cycles according to an embodiment of the invention.

DETAILED DESCRIPTION

In the discussions that follow, various process steps may or may not bedescribed using certain types of manufacturing equipment, along withcertain process parameters. It is to be appreciated that other types ofequipment can be used, with different process parameters employed, andthat some of the steps may be performed in other manufacturing equipmentwithout departing from the scope of this invention. Furthermore,different process parameters or manufacturing equipment could besubstituted for those described herein without departing from the scopeof the invention.

These and other details and advantages of the present invention willbecome more fully apparent from the following description taken inconjunction with the accompanying drawings.

Various embodiments of the invention describe a low cost andenvironmentally benign chemical reaction-deposition method to immobilizesulfur (S) on quasi-2-dimensional graphene oxides (GO) to preparegraphene oxide-sulfur (GO-S) nanocomposite cathodes for Li/S cells inionic liquid-based electrolytes. FIG. 1 a shows a scanning electronmicroscope (SEM) image of a GO-S nanocomposite. FIG. 1 b illustrates thestructure and properties of graphene oxide (GO) which may depend on aparticular synthesis method and degree of oxidation. The illustrated GOstructure comprises functional groups including a) epoxy bridges, b)hydroxyl groups, and c) pairwise carboxyl groups. GO typically preservesthe layer structure of the parent graphite, but the layers are buckledand the interlayer spacing is about two times larger (˜0.7 nm) than thatof graphite. Strictly speaking “oxide” is an incorrect but historicallyestablished name. Besides oxygen epoxide groups (bridging oxygen atoms),other functional groups experimentally found are: carbonyl (═CO),hydroxyl (—OH), and phenol groups attached to both sides. There isevidence of “buckling” (deviation from planarity), folding and crackingof graphene oxide sheets upon deposition of the layers on a choice ofsubstrate.

In one embodiment, nano-S was deposited onto graphene oxide (GO) sheetsby a chemical reaction-deposition method (see below experimental detailssection for further details). Then, the as-synthesized samples were heattreated in an argon (Ar) environment at low temperature (155° C.) for 12hours in order to remove some of the bulk S which is not directlyattached to the GO layers. When the as-synthesized GO-S nanocompositeswere heat-treated in Ar, the bulk S on the external surface of the GOmelted and diffused into the pores of the GO due to the strongadsorption effects derived from both the high surface area and thefunctional groups on the surface of the GO. At the same time, thislow-temperature heat treatment process can partially remove and/orchemically modify some of the functional groups on the GO surface andimprove the electronic conductivity of the as-prepared GO-Snanocomposites (See Table 1 below, wherein these materials were heattreated in Ar environment at 155° C. for 12 hour).

TABLE 1 Conductivities of the prepared materials. Heat treated GO-SSample name GO Heat treated GO nanocomposites Conductivity (S cm⁻¹)0.00129 0.316 0.105

FIG. 1 a shows the SEM image of the as-prepared GO-S nanocomposite afterheat treatment. The layer-like extremely conjugated nanostructures witha highly developed porous structure are clearly illustrated. Theenergy-dispersive X-ray (EDX) microanalysis in FIG. 1 c confirms theexistence of S in the composites. As indicated in a thermo gravimetricanalysis (TGA), about 66 wt % S is incorporated into the GO after heattreatment. FIG. 5 illustrates a TGA curve of GO-S nanocomposite recordedin N₂ with a heating rate of 10° C. min⁻¹ before (a) and after (b) heattreatment in Ar environment at 155° C. for 12 hours; (c) Pure GO afterheat treatment in Ar environment at 155° C. for 12 hours. From the TGAresult (c), it is clear that the mass loss due to the loss of functionalgroups from the pure GO after heat treatment in Ar environment at 155°C. for 12 hours is very small (˜3%). The mass loss due to the loss offunctional groups from GO-S upon heating GO-S nanocomposites should beeven smaller. Therefore, we are able to calculate the S content of theGO-S nanocomposite using the TGA data according to an embodiment of theinvention.

The transmission electron microscope (TEM) image in FIG. 2 a and theelectron energy-loss spectrum (EELS) in FIG. 2 d indicate that a thinlayer of S with a thickness of tens of nanometers is homogenouslydispersed on the flake-like GO surface with no significant fraction ofbulk S exposed on the external surface of the sample after heattreatment (For comparison, see the FIGS. 6 a,b SEM images for pure GOand FIGS. 7 a,b SEM images and FIGS. 7 c,d TEM images for GO-Snanocomposites before heat treatment). The corresponding elementalmapping of carbon (FIG. 2 b), and S (FIG. 2 c) display a very similarintensity distribution, revealing a homogeneous S coating on the GOflakes in the as-formed GO-S nanocomposites.

The unique structure of the GO-S nanocomposite can improve the overallelectrochemical performance when it is used as a cathode material forLi/S batteries. Firstly, it can accommodate the significant volumechanges of the S as it is converted to Li₂S on discharge, and back toelemental S on recharge. In addition, the partially reduced GO with itslarge surface area along with ubiquitous cavities can establish moreintimate electronic contact with the S and avoid their aggregation andloss of electrical contact with the current collector. Secondly, thelow-temperature heat-treated GO still contains various types offunctional groups. FIG. 9 illustrates ATR-FTIR spectra of GO. The bandsat 1103 cm⁻¹, 1226 cm⁻¹, and 1751 cm⁻¹ can be assigned to C—O stretchingvibrations, C—OH stretching vibrations, and C═O stretching vibrationsfrom carbonyl/carboxylic groups, respectively. The GO was heat treatedin Ar at 155° C. for 12 hours. These functional groups can have strongadsorbing ability to anchor S atoms and to effectively prevent thesubsequently formed Li polysulfides from dissolving in the electrolyteduring cycling.

Calculations were performed, ab initio, to clarify the role offunctional groups on GO in immobilizing S (see the calculation methodsand detailed results section below). The results indicated that bothepoxy and hydroxyl groups can enhance the binding of S to the C—C bondsdue to the induced ripples by the functional groups (see FIG. 3 a). Wealso performed a soft X-ray absorption spectroscopy (XAS) measurementwhich probes unoccupied electronic structure and thus is a powerful toolfor probing chemical bonding in surface chemistry. FIG. 3 b shows thecarbon K-edge absorption spectra for both GO and GO-S nanocomposites(see also S L-edge spectrum in FIG. 11). The absorption features “A”,“D” and “E”, which can be attributed to the π* state, excitonic state,and σ* state, respectively, are observed for both samples. Of note inthe spectra is the increase in the sharpness of the π* and excitonicstate for GO-S nanocomposites as compared with GO, suggesting that theordering of the sp²-hybridized carbon structure is better formattedafter S is incorporated. In addition, feature “C” originating fromdifferent functional groups (possibly C—O bond) on the GO are weakenedsignificantly when incorporated with S, which means a strong chemicalinteraction between S and functional groups of GO happens and S canpartially reduce the GO. In addition, a new feature “B” originated fromthe C—S σ* excitations, is observed for the GO-S nanocomposites.

We evaluated the electrochemical Li storage capability of theseheat-treated GO-S nanocomposites as potential cathode materials for Li/Scells in the n-methyl-(n-butyl) pyrrolidiniumbis(trifluoromethanesulfonyl)imide (PYR₁₄TFSI), Libis(trifluoromethylsulfonyl)imide (LiTFSI), and poly(ethylene glycol)dimethyl ether (PEGDME, M_(w)=250) mixture-based electrolyte.

FIG. 4 (a) shows the cyclic voltammetry (CV) profile of one electrode.The measurement was conducted at a scan rate of 0.05 mVs⁻¹ in thevoltage range of 1.0 to 3.6V vs Li/Li⁺. During the first cathodic scan,three main reduction peaks at around 2.4, 2.1, and 1.8 V were clearlyshown. According to the reported mechanisms for oxidation and reductionof S during discharge/charge, the peak at around 2.4V can be assigned tothe reduction of elemental S to higher-order Li polysulfides (Li₂S_(n),n≧8). The peak at about 2.1V probably corresponds to the reduction ofhigher-order Li polysulfides to lower-order Li polysulfides (such asLi₂S₆, Li₂S₄) from Li₂S₈. The peak at 1.8V is related to the reductionof polysulfide species to form Li₂S.

In the subsequent anodic scan, only one sharp oxidation peak is observedat about 2.6V that is attributed to the complete conversion of Li₂S andpolysulfides into elemental S. The main reduction peak is shifted toslightly higher potential and the oxidation peaks to lower potentialswith increase in cycle number, indicating an improvement ofreversibility of the cell with cycling. In addition, as the cycle numberincreased, the oxidation peak at 2.6V becomes less significant, whileanother new one at 2.35 V grows higher in intensity. The oxidation peakat 2.35V is associated with the formation of Li₂S_(n) (n>2). After thesecond cycle, both the CV peak positions and peak currents undergo verysmall changes, indicating relatively good capacity retention. The CVresults show that GO can help to prevent S from dissolving into theelectrolyte because of its large surface along with some functionalgroups on the surface.

FIG. 4 (b) depicts the first and second cycle discharge/charge typicalvoltage profiles of the electrodes at the 0.02 C rate (1C=1675 mA g⁻¹)between 1.0 and 3.0V (The capacity values in this description arecalculated according to the mass of S). All the discharge curves showthree plateaus in the voltage profile that are consistent with the peaksin the CV and are also well documented in the literature. The GO-Snanocomposite delivers a high initial discharge capacity of about 1320mAh g at 0.02 C. The corresponding coulombic efficiency in the firstdischarge/charge cycle is 96.4%. At the second cycle, a large reversiblecapacity of about 1247 mAh is preserved (97.5% coulombic efficiency),corresponding to about 94.5% capacity retention. This initial capacityloss is small compared to the formerly reported results of similarmaterials.

FIG. 4 (c) shows the cycling performance of the same cell cycled at arate of 0.1 C after the initial 2 cycles at 0.02 C. The dischargecapacity of the first cycle at 0.1 C remains at around 1000 mAh g⁻¹. Atthe second cycle at 0.1 C, this value decreases to about 950 mAh g⁻¹.However, after more than 50 cycles at the same rate, the reversiblecapacity remains at 954 mAh g⁻¹ (with a coulombic efficiency of about96.7%), indicating very stable reversibility of the electrochemicalreactions and excellent capacity retention. The cycle performance ofanother coin cell is further illustrated in FIG. 14. The cyclingperformance of GO-S nanocomposite cathode at a constant rate of 0.05 Cafter an initial activation processes at 0.02 C for 2 cycles. The GO-Snanocomposite was heat treated in Ar at 155° C. for 12 hours. The Scontent of the GO-S nanocomposite was 66 wt %, and the S content of thecathode (including carbon black and binder) was 46.2 wt %. In sum, theGO-S nanocomposites display improved coulombic efficiencies compared toformer reports.

The discharge capacity of the GO-S was highly reproducible over manycoin cells. Another example of the electrochemical performance of theGO-S electrode is demonstrated in FIG. 4 (d) where a cell showed areversible capacity of 735 mAh g⁻¹ at 0.5 C after 40 cycles at variousrates. Further cycling at a low rate of 0.05 C brings it back to areversible capacity of about 1100 mAh g⁻¹ for another 20 cycles. Whenthis coin cell was discharged at a higher rate of 1 C, a reversiblecapacity of about 550 mAh g⁻¹ was obtained. The last decrease of therate to 0.2 C, yielded a reversible capacity of about 890 mAh g⁻¹. Whenthis coin cell was further discharged at 2 C, an acceptable reversiblecapacity of about 370 mAh g⁻¹ was obtained, indicating excellentcapacity reversibility and high rate performance even after 100 cycles.

FIG. 15 illustrates a typical discharge/charge profiles (potential vs.capacity) at various C rates for GO-S nanocomposite cathode. The GO-Snanocomposites were heat treated in Ar at 155° C. for 12 hours. The Scontent of the GO-S nanocomposite was 66 wt %, and the S content of thecathode (including carbon black and binder) was 46.2 wt %.

The GO clearly performs very well as a means to stabilize the Selectrode. The GO provides highly reactive functional groups on itssurface that can serve as immobilizers to hold the S. Also by limitingthe concentration of the polysulfide anions in the electrolyte, theredox shuttle phenomenon is largely avoided. The intimate contact of theS provided by the large surface area and the functional groups on GO isfavorable to good electron/ion accessibility, leading to enhanced cycleperformance and rate capability. In addition, the optimized ionicliquid-based electrolytes which have suitable viscosities and wettingproperties influence the penetration of electrolyte into the S electrodestructure, while increasing the ionic conductivity within the electrodesat the same time.

A control experiment in LiTFSI-PEGDME-based electrolyte is described inrelation to FIG. 16 which illustrates a cycling performance of GO-Snanocomposite cathode at a constant rate of 0.1 C after an initialactivation processes at 0.02 C for 2 cycles. The GO-S nanocompositeswere heat treated in Ar at 155° C. for 12 hours.

From FIG. 16, we can see that the GO-S nanocomposite cathode has a veryhigh initial reversible capacity of about 1304 mAh g⁻¹ at 0.02 C withthe corresponding coulombic efficiency of about 94.7% in theLiTFSI-PEGDME electrolyte. After two cycles' activation at 0.02 C, alarge discharge capacity of about 1014 mAh g⁻¹ still can be delivered atthe first cycle at 0.1 C with a corresponding coulombic efficiency ofabout 100%. However, after 16 cycles at 0.1 C, the capacity is about 736mAh g⁻¹, and the corresponding coulombic efficiency is only about 69.7%.

This control experiment shows that the use of the ionic liquid-basedelectrolyte (PYR₁₄TFSI-LiTFSI-PEGDME mixture, as shown in the main textof the paper) can definitely help the improvement of the electrochemicalperformance of GO-S based Li/S cells. On the other hand, the previousresearch results indicated that when using PYR₁₄TFSI-LiTFSI-PEGDMEmixture as electrolyte in the Li/S cells with other C—S nanocomposite(not GO-S) cathodes, the capacity fading is clear. These resultsdirectly support our conclusion that the GO clearly performs very wellas a means to stabilize the S in our GO-S electrode, while usingionic-liquid based electrolyte can further enhance the performance.

In summary, a novel chemical reaction-deposition method is employed tosynthesize a GO-S nanocomposite to immobilize S in the cathode materialof Li/S cells. The GO-S nanocomposite cathodes display goodreversibility, excellent capacity stability of about 1000 mAh g⁻¹, andrate capability of up to 2 C in ionic liquid-based electrolyte. The GOin the heat-treated composites have good conductivity, extremely highsurface-area, and provide a robust electron transport network. Thefunctional groups on the GO surface play the role of immobilizers thatkeep intimate contact of the conducting matrix with S species, andeffectively confine any polysulfides from dissolving. The GO networkalso accommodates the volume change of the electrode during the Li—Selectrochemical reaction. As a result, reversibility and high ratedischarge capability were obtained. The same strategy could be helpfulto explore and develop new porous carbon, or conductive polymer based Snanocomposite cathodes for advanced Li/S cells.

Experimental Details Chemicals.

Graphite powder, sodium nitrate (NaNO₃), potassium permanganate (KMnO₄),96% sulfuric acid (H₂SO₄) solution, 30% hydrogen peroxide (H₂O₂)solution, sodium sulfide (Na₂S, anhydrous, Alfa Aesar), sublimed Spowder (99.9%, Mallinckrodt), formic acid (HCOOH, 88%, Aldrich),N-methy-N-butylpyrrolidinium bis(trifluoromethanesulfonyl) imide(PYR₁₄TFSI, ≧98.0%, Aldrich), poly(ethylene glycol) dimethy ether(PEGDME, M_(w)=250, Aldrich) and lithiumbis(trifluoromethylsulfonyl)imide (LiTFSI, 99.95%, Aldrich) were usedwithout further treatment.

Synthesis of the Graphene Oxides.

The graphene oxide used in an embodiment of the invention is exfoliatedfrom graphite oxide prepared using the following method. Graphite oxidewas prepared using a modified Hummers method. Firstly, 0.2 g of naturalgraphite powder and 0.175 g of NaNO₃ were placed in a three-necked flaskwith a stirrer chip. Then 15 ml of 98% H₂SO₄ was slowly added. Themixture was stirred in an ice water bath environment for about 2 hoursfollowed by gradually adding 0.9 grams of KMnO₄ (purity 99%) over about2 hours under slow stirring conditions. The as-formed mixture wasallowed to react for five days at room temperature. Afterwards, 20 ml of5 wt % H₂SO₄ aqueous solution was added over the course of about 1 hwith stirring. The resultant mixture was further stirred for 2 hfollowed by adding 0.6 ml of 30 wt % H₂O₂ aqueous solution and stirredfor another 2 h. This solution was continuously washed thoroughly with amixed aqueous solution of 3 wt % H₂SO₄/0.5 wt % H₂O₂ many times, andthen the purification procedure was similarly repeated three more timesusing deionized (DI) water (Millipore, 18.2 MΩcm). The resultant mixturewas dispersed in DI water and then centrifuged to remove ions of oxidantorigins. The remaining dispersion was purified by repeating the sameprocedures 20 times with DI water. Finally, a brown-black homogeneousgraphite oxide dispersion was obtained. In this embodiment, 180 mg ofgraphite oxide was suspended in 180 ml ultrapure water (Millipore, 18.2MΩcm), and then sonicated at 50° C. for 5 hours to form a stablegraphene oxide (GO) dispersion.

Preparation of Sodium Polysulfide Solution.

0.58 g Na₂S was added into a flask that has been filled with 25 mldistilled water to form a Na₂S solution, then 0.72 g elemental S wassuspended in the Na₂S solution and stirred with a magnetic stirrer forabout 2 hours at room temperature. The color of the solution changedslowly to orange-yellow as the sulfur dissolved. After dissolution ofthe sulfur, a sodium polysulfide (Na₂S_(x)) solution was obtained (Itshould be noted that through controlling the ratios of Na₂S andelemental S, we adjust the value of x in Na₂S_(x), this will furthercontrol the S content in the as following prepared GO-S composites).

Na₂S+(x−1)S→Na₂S_(x)

Synthesis of Graphene Oxide-Sulfur Composite.

The novel graphene oxide-sulfur (GO-S) composite was prepared by achemical deposition method in an aqueous solution. 180 mg of graphiteoxide was suspended in 180 ml ultrapure water (Millipore, 18.2 MΩcm),and then sonicated at 50° C. for 5 hours to form a stable graphene oxide(GO) dispersion. Then, the Na₂S_(x) solution was added to theabove-prepared GO dispersions in the presence of 5 wt % surfactant cetyltrimethylammonium bromide (CTAB), the as-prepared GO/Na₂S_(x) blendedsolution was sonicated for another 2 hours and then directly titratedinto 100 ml of 2 mol/L HCOOH solution at a rate of 30-40 drops/min andstirred for 2 hours. Finally, the precipitate was filtered and washedwith acetone and distilled water several times to eliminate salts andimpurities. After filtration, the precipitate was dried at 50° C. in adrying oven for 48 hours.

S_(x) ²⁻+2H⁺→(x−1)S+H₂S

Heat treatment of GO-S composites. The as-synthesized GO-S compositeswere heat treated in a sealed vessel under flowing argon with controlledflow rate of about 200 cc S⁻¹ at 155° C. for 12 h. In order to furtherdecrease the S content, some of the as-synthesized samples were alsoheat treated in the same argon environment at 160° C. for 12 h.

Cell Assembly and Testing.

CR2032-type coin cells were fabricated by sandwiching a porouspolypropylene separator (Celgard 3501, Hoechst Celanese) between theheat treated GO-S nanocomposite electrode and a lithium metal foil(Cyprus Foote Mineral, 99.98%, USA) in a high-purity argon-filled glovebox. 1 mol/kg LiTFSI in PYR₁₄TFSI/PEGDME (1:1, by weight) solution wasused as the electrolyte. The GO-S working electrodes were prepared bymixing the GO-S nanocomposite, carbon black, and polyvinylidenedifluoride (PVDF) at a weight ratio of 70:20:10 in NMP solvent to form aslurry. The resultant slurry was uniformly spread via doctor blade onpure aluminum foil and dried at 50° C. for 72 hours. The final S contentof the cathode material is 46.2 w/o. Cyclic voltammogram (CV)measurements were performed on an AQ4 Gamry Reference 600electrochemical workstation with a voltage range from 1.0 to 3.6 V at ascan rate of 0.05 mV s⁻¹. Galvanostatic discharge and charge experimentsof the coin cells were conducted using an Arbin automatic battery cycler(BT-2000) at several different rates between cut-off potentials of 1.0and 3.0 V. All of the electrochemical performance measurements wereobtained at a constant temperature of 25° C.

Material Characterizations.

The samples were characterized using scanning electron microscopy (SEM:Zeiss Gemini Ultra-55) coupled with an energy dispersive X-rayspectrometer (EDX), transition electron microscope (TEM: 200 kV FEImonochromated F20 UT Tecnai), thermogravimetric analysis (TGA), X-raydiffraction (XRD) (Diffraktometer D500/501, Siemens), Hall effectmeasurement system (HMS-5000), Attenuated total reflection Fouriertransform infrared spectroscopy (ATR-FTIR) (Nicolet Avatar 360 with anOmni-Sampler ATR accessory), and X-ray photoelectron spectroscopy (XPS)(Surface Science Instruments S-probe spectrometer). The soft X-rayabsorption spectroscopy (XAS) measurements were performed on Beamline7.0.1 at the Advanced Light Source of Lawrence Berkeley NationalLaboratory. The energy resolution of monochromator was set to 0.1 eV forthe C K-edge and S L-edge XAS.

Computational Methods.

All the calculations were performed by using Vienna ab-initio simulationpackage (VASP). The Perdew-Burke-Ernzerhof (PBE) generalized gradientapproximation and the projector-augmented wave (PAW) potential with acutoff energy of 400 eV were used to describe the exchange-correlationenergy and the electron-ion interaction, respectively. We adopted a 5×5supercell geometry for graphene and the distance between two adjacentcarbon sheets is at least 10 Å. A k-mesh of 6×6×1 was used to sample theBrillouin zone. All the geometries were optimized without any symmetryconstraint until the residual force on each atom is less than 0.01 eV/A.Herein, two-sided configurations are considered for adsorption on GO.The binding energy of a pair of Sulfur atoms is defined as the energydifference between the reactants (graphene/GO and two S atoms) andproducts (the S-adsorbed complex), that isBE=E_(G/GO)+2E_(S)−E_(G/GO-2S). Detailed calculated results are shown inFIG. 10.

FIG. 8 illustrates XRD patterns of GO-S nanocomposites before (a) andafter heat treatment in Ar environment for 12 h at differenttemperatures of (b) 155° C., and (c) 160° C. The crystallized Snanoparticles were observed under the high-resolution TEM (HRTEM)imaging mode, as shown below in FIG. 17 d. However, we cannot excludethe possibility that there are some larger S crystallites in the thickerregion of the samples (residues of those seen in FIG. 7 before heattreatment) that could also contribute to the XRD patterns.

FIG. 10 illustrates calculated results (yellow, red and white ballsdenote S, O and H atoms, respectively, while the others, blue, arecarbon atoms): First, we calculate two S atoms adsorption on grapheneseparately FIG. 10( a) and in pair FIG. 10( b). The binding energies are1.64 and 2.08 eV, respectively, which can be viewed as the lower andhigher bounds of S adsorption. Then we study the effect of adsorbedepoxy groups on the adsorption of two S atoms. It is found that Sadsorption can be significantly enhanced by epoxy groups, depending onthe distance between the functional group and S atom. Typically, thebinding energies are 1.82 eV and 2.03 eV for the adsorptionconfigurations shown in FIG. 10( c) and FIG. 10( d). Note that thelocations of S atoms are the same as that in FIG. 10( a), where thebinding energy is 1.64 eV. The enhancement effect of the epoxy decreaseswith increasing distance between S and the epoxy group. Additionalcalculations show that the hydroxyl group exhibits a similar trend. FIG.10( e) and FIG. 10( f) give the binding energy of 1.66 and 2.84 eV,indicating that the effect of hydroxyl group is more local than that ofthe epoxy. A surprising result is that S atoms can also insert into theO—H bond (g), with a much larger binding energy of 4.05 eV. However, thedynamic factor may hinder its formation.

FIG. 11 illustrates S L-edge XAS spectrum of GO-S nanocomposites afterheat treatment in Ar at 155° C. for 12 hours. It confirms the existenceof S in the composites. The soft X-ray absorption spectroscopy (XAS)measurements were performed on Beamline 7.0.1 at the Advanced LightSource. The energy resolution of monochromator was set to 0.1 eV for theS L-edge XAS.

FIG. 12 illustrates FTIR spectra of (a) GO, and (b) GO-S nanocomposites.These materials were heat treated in Ar at 155° C. for 12 hours.According to the literature reports, the 1220 cm⁻¹ indicates the C—OHstretching vibrations, the ˜1200 cm⁻¹ can be assigned to C—O stretch,while the characteristic feature at ˜1204.5 cm⁻¹ in GO-S nanocomposites(while it is absent in GO) may indicate the existence of C—S bond in theas-synthesized GO-S nanocomposites after thermal treatment.

FIG. 13 illustrates XPS spectra of (a) GO, (b) S element, and (c) GO-S.The GO and GO-S were heat treated in Ar at 155° C. for 12 hours. In theS 2p_(3/2) region, XPS of GO-S nanocomposites show one peak at S2p_(3/2) binding energy of about 164.0 eV with a slight wider fullwidths at half maximum intensities (FWHM) than that of elemental S. Inthe S is region, XPS of GO-S nanocomposites show one peak at S1s bindingenergy of about 228.0 eV with a slight wider full widths at half maximumintensities (FWHM) than that of elemental S. These chemical shifts ofS2p_(3/2) and S is regions may indicate that there have interactionsbetween S and GO in the GO-S nanocomposites.

FIG. 17 illustrates SEM (a, b) and TEM (c, d) images of theas-synthesized GO-S nanocomposites after heat treatment in Ar at 160° C.for 12 hours. In the high-resolution TEM (HRTEM) image (d), somecrystallized S nanoparticles are highlighted by arrows.

FIG. 18 illustrates an electrochemical evaluation of GO-S nanocompositecathodes made by a different process from that in the description above.The GO-S nanocomposites were heat treated in Ar at 160° C. for 12 hours.The S content in the GO-S nanocomposite was about 40 wt %, and the Scontent in the cathode (including carbon black and binder) was about 28wt %. (a) CV curve of a GO-S nanocomposite cathode at 0.05 mV s⁻¹scanning rate; (b) Galvanostatic charge/discharge profiles of GO-Snanocomposite cathode at 0.02 C rate; (c) cycling performance of GO-Snanocomposite cathode at a constant current rate of 0.1 C after aninitial activation processes at 0.02 C for 2 cycles; (d) Reversiblecapacity vs. current density (rate capability) for GO-S nanocompositecathode. All the cells were cycled in the potential window from 1.0 to3.0 V.

Note that the capacity values are normalized to the initial dischargecapacity. Also note that the first discharge capacity curve is inabnormal shape (b). We can also see an extra reduction current at lowervoltage region in the first cycle of the CV curve (a). These featuresmay come from some irreversible electrochemical reactions related to theGO, because this abnormal initial discharge is only significant insamples with lower S loading (i.e. higher GO content; we did not observesuch abnormal behavior in the samples prepared using the processdescribed above-FIGS. 4, 14, and 15). Nevertheless, these results showthat GO-S (even though it is processed differently) can help to improvethe capacity retention, coulombic efficiency, and rate capacity of theLi/S cells.

FIG. 19 illustrates cycling performance of a pure GO cathode at aconstant rate of 0.1 C after an initial activation processes at 0.02 Cfor 2 cycles. The GO was heat treated in Ar at 155° C. for 12 hoursbefore assembling coin cell. The result indicates that the GO phasecontributes essentially nothing to the capacity, because at thepotentials of the S electrode, GO does not intercalate lithium at all.

What is claimed is:
 1. A composition of matter comprising: a grapheneoxide-sulfur (GO-S) nanocomposite, wherein GO further comprises aplurality of functional groups and S is bonded to carbon atoms.
 2. Thecomposition of matter of claim 1, wherein the plurality of functionalgroups includes at least one functional group selected from the groupconsisting of an epoxy bridge, a hydroxyl group, a phenol group, and acarbonyl group.
 3. An electrode comprising: a graphene oxide-sulfur(GO-S) nanocomposite.
 4. The electrode of claim 3, wherein the electrodeis a cathode.
 5. The electrode of claim 3, wherein the GO-Snanocomposite further comprises a plurality of functional groups and Sis bonded to carbon atoms.
 6. The electrode of claim 5, wherein theplurality of functional groups includes at least one functional groupselected from the group consisting of an epoxy bridge, a hydroxyl group,a phenol group, and a carbonyl group.
 7. A battery comprising: agraphene oxide-sulfur (GO-S) nanocomposite cathode; a separator; ananode; and an electrolyte.
 8. The battery of claim 7, wherein theseparator is a porous polypropylene.
 9. The battery of claim 8, whereinthe porous polypropylene is a Celgard
 3501. 10. The battery of claim 7,wherein the electrolyte is an ionic liquid-based electrolyte.
 11. Thebattery of claim 10, wherein the electrolyte is PYR₁₄TFSI-LiTFSI-PEGDME.12. The battery of claim 7, wherein the electrolyte is LiTFSI-PEGDME.13. The battery of claim 7, wherein the graphene oxide-sulfur (GO-S)nanocomposite cathode further comprises carbon black, and polyvinylidenedifluoride (PVDF).
 14. The battery of claim 7, wherein the grapheneoxide-sulfur (GO-S) nanocomposite cathode comprises GO-S nanocomposite,carbon black, and polyvinylidene difluoride (PVDF) at a weight ratio of70:20:10, respectively.
 15. The battery of claim 13, wherein the cathodefurther comprises an aluminum substrate.
 16. The battery of claim 7,wherein the GO-S nanocomposite further comprises a plurality offunctional groups and S is bonded to carbon atoms.
 17. The battery ofclaim 16, wherein the plurality of functional groups includes at leastone functional group selected from the group consisting of an epoxybridge, a hydroxyl group, a phenol group, and a carbonyl group.
 18. Amethod of preparing a graphene oxide-sulfur (GO-S) nanocompositecomprising: providing a graphene oxide (GO) dispersion; adding a sodiumpolysulfide (Na₂S_(x)) solution to the GO dispersion to form a blendedsolution; titrating the GO/Na₂S_(x) blended solution into a HCOOHsolution to form a precipitate; and heat treating, for a specified timeand temperature, the precipitate in a sealed vessel utilizing a flowinggas at a specified gas flow rate.
 19. The method of claim 18, whereinthe flowing gas is argon.
 20. The method of claim 18, wherein the gasflow rate is approximately 200 cc S⁻¹.
 21. The method of claim 18,wherein the temperature is approximately 155° C.
 22. The method of claim18, wherein the time is approximately 12 hours.
 23. The method of claim18, wherein the Na₂S_(x) solution is added to the GO dispersion in thepresence of 5 wt % surfactant cetyl trimethylammonium bromide (CTAB).24. The method of claim 18, wherein the sodium polysulfide (Na₂S_(x))solution is prepared by adding Na₂S into a flask that has been filledwith distilled water to form a Na₂S solution, then elemental S issuspended in the Na₂S solution, wherein the ratios of Na₂S and elementalS, are adjusted to determine a value of x in Na₂S_(x).
 25. The method ofclaim 24, wherein approximately 50-90 wt % S is incorporated into the GOafter the heat treatment.
 26. The method of claim 25, whereinapproximately 60-70 wt % S is incorporated into the GO after the heattreatment.
 27. The method of claim 18, wherein the graphene oxide (GO)dispersion is prepared by exfoliating GO from a graphite oxide.
 28. Themethod of claim 27, wherein the graphite oxide was prepared using amodified Hummers method.